C45E
In the range of special steels, C45E is the best compromise between resistance and toughness. This is the feature that takes this product to the widest diffusion around whole Europe. Usually allocated to heat-treatment, frequently used in the mecchanical industries for the production of axles, levers, crank handles, linchpins, etc.
Quality C45E
Categoria Acciai speciali, acciai al carbonio
Norma di rif EN 10083 – 2: 2006
Numero 1.1191
Categoria Acciai speciali, acciai al carbonio
Norma di rif EN 10083 – 2: 2006
Numero 1.1191
CHIMICAL COMPOSITION
Cr+Mo+Ni max 0.63%.
C45R n• 1.1201 S% 0.020-0.040. Permissible deviations on the product ± 0.005.
C45 n• 1.0503 S% eP% max 0. 045. Permissible deviations on the product ± 0.005.
Calcium (Ca) treatment may be supplied on reguest
C45R n• 1.1201 S% 0.020-0.040. Permissible deviations on the product ± 0.005.
C45 n• 1.0503 S% eP% max 0. 045. Permissible deviations on the product ± 0.005.
Calcium (Ca) treatment may be supplied on reguest
MECHANICAL PROPERTIES
C45E Hot-formed-hot-rolled-rod mechanichal properties for normalized condition EN 10083-2: 2006
(*) Testing at room temperature (longitudinal)
C45E Hot-formed-hot-rolled-rod mechanichal properties for quenched and tempered condition EN 10083-2: 2006
(*) Testing at room temperature (longitudinal)
Table of tempering values at room temperature for round Ø 10 mm after guenching at 840 °C in water
20MnV6
This is micro-alloyed steel with improved weldability compared to C45E. Thanks to its mechanical structure provides the best performance at low temperatures. It is produced exclusively in the natural state.
It is a steel in great demand in the countries of northern Europe.
It is a steel in great demand in the countries of northern Europe.
Quality 20MnV6
Werkstoff nr. 1.5217
Werkstoff nr. 1.5217
CHIMICAL COMPOSITION
MECHANICAL PROPERTIES
Hot-rolled untreated +U
(*) Testing at room temperature (longitudinal)
Hot-rolled guenched and tempered +QT
(*) Testing at room temperature (longitudinal)
REFERENCE STANDARDS IN THE WORLD
CHIMICAL COMPOSITION
42CrMoS4 n° 1.7227 S% 0.020-0.040 Permissible deviations on the product ± 0.005%.
Calcium (Ca) treatment may be supplied an reguest
Calcium (Ca) treatment may be supplied an reguest
MECHANICAL PROPERTIES
Hot-formed - hot-rolled- rod mechanical properties for quenched and tempered condition EN 10083-3: 2006
(*) Testing at room temperature (longitudinal)
Table of tempering values at room temperature for round Ø 10 mm after guenching at 850°C in oil
Tubes E355 + SR
These tubes are cold drawn micro-alloyed, low carbon weldable. They have a good combination of strength and toughness with excellent machinability and weldability. It is often used in hydraulic market.
Qualità Tubi E355
Categoria Acciaio per impieghi meccanici
Norma di rif. EN 10305-1
Categoria Acciaio per impieghi meccanici
Norma di rif. EN 10305-1
CHIMICAL COMPOSITION
MECHANICAL PROPERTIES
Hot-rolled guenched and tempered +QT
(*) Testing at room temperature (longitudinal)
Modercromo treatments
ISOCROM® 1000h
Corrosion resistance up to 72 hours of CASS test.
Innovative flagship product of our production with unique results.
MORE INFORMATION
MORE INFORMATION
ISOCROM® 1000h
Corrosion resistance up to 1000 hours (based on UNI EN ISO 9227 Neutral Salt Spray). Standard production product with excellent quality results.
MORE INFORMATION
MORE INFORMATION
ISOCROM® 500h
Corrosion resistance up to 500 hours (based on UNI EN ISO 9227 Neutral Salt Spray). Standard production product with excellent quality results.
MORE INFORMATION
MORE INFORMATION
ISOCROM® 200h
Corrosion resistance up to 200 hours (based on UNI EN ISO 9227 Neutral Salt Spray).
Standard production product with good quality results.
MORE INFORMATION
Standard production product with good quality results.
MORE INFORMATION